Chemical vapor deposition system for polycrystalline silicon rod production

ABSTRACT

Disclosed are processes and reactor apparatus for rapidly producing large diameter, high-purity polycrystalline silicon rods for semiconductor applications. A.C. current is provided to the rods by a power supply, having a fixed or variable high frequency in the range of about 2 kHz to 800 kHz, to concentrate at least 70% of the current in an annular region that is the outer 15% of a rod due to the &#34;skin effect.&#34;

This application claims the benefit of U.S. Provisional Application No. 60/069,596, filed Dec. 15, 1997, incorporated herein by reference.

BACKGROUND OF THE INVENTION

The present invention relates to a process and equipment for the production of high-purity polycrystalline silicon in rod form for semiconductor applications. The polycrystalline silicon is used as the raw material in the fabrication of single crystal silicon for semiconductors by the CZ (Czochralski) method or the FZ (float zone) method.

The most common method of producing polycrystalline silicon, which is a raw material used for the production of single crystal silicon for semiconductors, has been to deposit silicon on starter filaments by thermal decomposition of a chloride-type silane, such as trichlorosilane, so as to produce silicon rods. Such a process is described in U.S. Pat. No. 4,724,160 of Arvidson et al. Japanese Patent Laid-Open No. 56-105622 discloses a reactor structure using a chloride-type silane in which a large number of electrodes are arranged on a circular plate and a large number of silicon starter filaments are arranged in a reverse-U-shaped or a square-reverse-U-shaped form.

Another method involves the production of polycrystalline silicon from monosilane gas, which is another common starting material. Silicon starter filaments are heated inside the reactor. At a temperature of several hundred degrees or more, monosilane gas decomposes and deposits on heated filaments to form larger-diameter silicon rods. The rods may be thermally insulated from each other so as to prevent vapor-phase temperature rise and as to eliminate thermal influences from the adjacent heated silicon rods, thereby obtaining uniform silicon deposition.

Polycrystalline silicon, in the form of rods or chunks obtained by crushing rods, is being widely used in the production of single crystal silicon by the CZ or FZ method. A high purity level and competitive cost are particularly required of polycrystalline silicon rods for semiconductor applications.

In both of the silicon deposition systems described above, a power supply is used to pass current through the rods for such heating rods. The existing power supplies for the thermal decomposition furnaces, such as that shown in U.S. Pat. Nos. 4,147,814 and 4,150,168 of Yatsurugi et al., and U.S. Pat. No. 4,805,556 of Hagan et al., and U.S. Pat. No. 5,478,396 of Keck et al., produce up to 2000 amps of current at 60 Hz. Power supplied at this low 60 Hz frequency (or the European standard power frequency of 50 Hz), allows the heating current to flow throughout the rod's cross-section during thermal decomposition.

When power is supplied at 60 Hz, the current migrates toward the centers of the rods. The center of a rod becomes progressively hotter, relative to the surrounding outer region of the rod, since the center is thermally insulated by the outer region or “skin” of the rod. Heating at the center causes electrical resistance to decrease at the center, since r=f(1/T). The lower resistance causes even more current to flow through the center, which creates more heat. Since a majority of the current flows through the center of the rod when operating at 60 Hz, the center of a rod becomes considerably hotter than the skin portion of the rod. This uneven temperature profile in turn creates internal thermal stresses when the rods cool down following growth, with the resulting rods being brittle and subject to breakage. In particular, when the power is turned off, the surface of the rod cools and contracts quickly to a given depth. The cooled surface acts as an insulative layer to the rod interior. Because of the insulative effect, the center of the rod cools at a much slower rate. The effect of this is that the center material has a lower specific volume, at the termination of cooling, due to the longer relaxation time. (The slower the cooling rate the longer the atoms have to arrange themselves. Thus, the interior of the rod should have a slightly higher density than the exterior.) This has the effect of radially pulling the surface into a compression state while the inner part of the rod is in a state of tension due to the smaller specific volume. It is easy to picture that, as the radius approaches zero, the stresses increase due to cooling rates that are progressively slower as ore approaches the center of the rod. Due to the stresses, to obtain commercially acceptable yields, rods produced with 60 Hz power supplies have been limited to a maximum diameter of about 150 mm.

SUMMARY OF THE INVENTION

Improved processes and equipment have been developed for the production of polycrystalline silicon in rod form for semiconductor applications by thermal decomposition of a highly refined silane or halosilane gas and deposition of silicon on a deposition surface. Using such processes and equipment, it is possible to produce a rod as large as 300 mm or more in diameter having a stress of no more than 11 megapascals (MPa) throughout the volume of the rod.

Such low stress rods can be formed by maintaining the entire volume of a silicon rod within a 50° C. temperature range during a majority of the time period during which silicon is deposited on the deposition surface. When this is done, the strength of polycrystalline silicon rods is increased so that rods having diameters of as much as 300 mm or more can be grown reliably. A high frequency power supply, that can produce current of a frequency in the range of 2 kilohertz to 800 kilohertz, can be used to maintain the entire volume of a silicon rod within the 50° C. temperature range during the deposition of silicon. Such a high frequency power source will concentrate the current on the surface of a growing rod due to the “skin effect” and thereby more uniformly heat the rod and decrease rod brittleness.

BRIEF DESCRIPTION OF THE DRAWING

In the drawings:

FIG. 1 is a schematic vertical sectional view showing a reactor according to the present invention for the production of high-purity polycrystalline silicon rods for semiconductor applications by the deposition of silicon from a silicon-bearing gas.

FIG. 2 is a sectional view taken along line 2—2 of FIG. 1 showing the cross section of a rod after it has been grown to a diameter greater than 150 mm.

FIG. 3 is a diagram of a control circuit for operation of a power supply of the type shown in FIG. 1.

FIG. 4 is a chart showing calculated temperature profiles for 150 mm diameter silicon rods heated by A.C. current.

FIG. 5 is a chart showing calculated radial stress profiles for 150 mm diameter silicon rods produced by heating with A.C. current.

DETAILED DESCRIPTION

FIG. 1 shows chemical vapor deposition (CVD) equipment for the production of high-purity polycrystalline silicon for semiconductor applications. In such a reactor, monosilane gas is decomposed and silicon is deposited at heated deposition surfaces of growing silicon rods. The illustrated reactor is similar to that disclosed in the above-mentioned U.S. Pat. No. 4,150,168 of Yatsurugi, et al., that is hereby incorporated herein by reference. A verger-type cover or bell 1 and a round base plate 2 provide a reactor vessel. A partition member 4, that is a heat exchanger or water jacket having a cooling water inlet pipe 5 and outlet pipe 6 and that is shaped to define multiple reaction chambers 3, is provided inside a cylindrical space defined by the cover 1 and base plate 2.

The cover 1 is least partially hollow and serves as a water cooled heat exchanger or cooling jacket. The lower surface of the cover 1 serves as the reactor vessel ceiling. Provided in the cover section are a cooling water inlet 1 c and a cooling water outlet 1 d. As it moves from the inlet 1 c to the outlet 1 d, cooling water flows through the space between the inner and outer walls of the cover. Electrodes 9 extend from below through the base plate 2, through the intermediation of insulating members 8, and are arranged at positions corresponding to the centers of the reaction chambers 3. Chucks 10 are attached to the tips of the electrodes 9 that are water cooled through inlet and outlet cooling pipes 7. The water flowing through the water cooling jacket may be replaced by another fluid cooling or a heating medium.

A reactant gas delivery pipe 11 extends upwardly from below through the base plate 2 and connects a plurality of gas nozzles 13 that are spaced to distribute monosilane gas along the reaction chambers 3. Provided inside each of the gas nozzles 13 is a capillary or an orifice to enable the monosilane gas to be ejected uniformly through the nozzles 13. An exhaust pipe 16 is used to remove spent reactant gas. Viewing windows 12 may be provided through the cover 1 and its cooling jacket to enable observation of the rods 14 during the deposition process. One or more sensors 23, such as pyrometers (not shown), may be used to monitor the surface temperature of rods growing in the reactor.

One or more power supplies are connected to the electrodes 9 to pass current through the rods 14 for heating rods. The system shown in FIG. 1, includes a low frequency power supply 20, a high frequency power supply 21, and a switch 22 suitable to connect one or the other of the power supplies 20, 21 to the electrodes 9. The low frequency power supply 20 supplies current at a relatively low frequency, such as the 60 Hz standard frequency (or the European standard power frequency of 50 Hz). The high frequency power supply 21 is capable of operating in the 2 kilohertz to 800 kilohertz range with an A.C. current amplitude in the range of 10 to 3000 amperes and a voltage amplitude in the range of 200 to 30,000 volts. Most advantageously, the high frequency power supply is of the type wherein the current can be varied through a range of frequencies. Conveniently the power supplies 20, 21 could be combined in a single, variable current power supply (not shown) that has integral switching circuitry and is capable of operating at both low and high frequencies.

Silicon initial rods or starter filaments 17 are positioned in the reaction chambers 3 and held at their lower ends by the chucks 10. A pair of silicon starter filaments 17 are connected to each other at their upper ends through a silicon bridge 18 to provide a U-shaped filament on which a silicon rod 14 is formed. Cooling water is circulated through the cover 1.

Because silicon is not very electrically conductive at ambient temperature, the silicon starter filaments 17 may be preheated to a desired temperature, typically at least 200° C., to increase their conductivity. The surfaces of the preheated filaments then can be maintained at an elevated temperature by supplying electricity to the filaments through the electrodes 9 so the surfaces can serve as silicon deposition surfaces. Preheating can be accomplished by supplying, a blast of hot inert gas through inlet 15 in the base plate 2 as described in U.S. Pat. No. 4,150,168 of Yatsurugi. Preheating can also be accomplished by operation of a radiant heat source (not shown) inside the reactor.

The filaments also may be preheated by directly supplying low frequency A.C. current thereto through the electrodes 9, as described in U.S. Pat No. 4,150,168, but at a high voltage. For example, filaments may be heated by applying a voltage as high as 30,000 volts at a frequency of 60 Hz. After the silicon heats up beyond a temperature of 200° C., its resistance decreases with increasing temperature, so it has “broken into conduction.” At that point, the voltage can be decreased to about 3,000 v and the 60 Hz current regulated to provide a desired silicon deposition surface temperature in the range of 600° C. to 1200° C. A silane gas, most advantageously monosilane gas, is fed into the reactor through the gas pipe 11 and the gas nozzles 13. While ascending inside the reaction chambers 3, that are heated by the silicon starter filaments 17, the gas reacts to deposit polycrystalline silicon 19 on the surfaces of the silicon starter filaments 17. The deposited silicon builds up to form polycrystalline silicon rods 14. Each starter filament 17 thus provides an initial silicon deposition surface, and after silicon is deposited on the filament, the outer surface of the deposited silicon serves as the deposition surface. With monosilane gas, best results are obtained when the deposition surface of a growing rod is maintained at a temperature of about 850° C. during deposition of silicon on the rods. Reactant gas that has been blown upwards beyond the reaction chambers 3 is removed through the exhaust pipe 16. While the growing silicon rods are small, the current can be as low as 20 amps. As the rods increase in diameter, the current necessary to keep the silicon deposition surface at a constant temperature steadily increases while the required voltage decreases.

At some point, determined by the measurement of one or more parameters such as elapsed time, current consumption, a product attribute such as rod diameter, surface temperature or the like, the 60 Hz current is turned off, for example by automated operation of the switch 22, and the rods are further maintained at a desired temperature by high frequency current supplied by the high frequency power source 21. For example, as illustrated in FIG. 3, a sensor or timer 23 signals a control system 24, preferably a computer control system, when a triggering event has occurred. The control system 24 then operates the switch 22, e.g. by operation of a solenoid, to engage the high frequency power supply 21. Because the high frequency power supply 21 provides alternating current in the 2 kilohertz to 800 kilohertz range, heating current migrates to the surface of a rod because of the “skin effect.” To take best advantage of the skin effect, the high frequency power supply should be configured to deliver current such that at least about 70% of the current is concentrated in an annular outer region 26 shown in FIG. 2, which outer region is the outer 15% of the radius of a rod being grown in a reactor. A lesser amount of current flows through a core or inner region 28 of the rod located inside the outer region 26. In general, it is desirable to keep the high frequency current frequency as low as possible, within the 2 kilohertz to 800 kilohertz range, to minimize inductive losses and so that equipment can be build using solid state components, which are frequency limited. It may also be advantageous to vary the frequency during the CVD process to further minimize the internal stresses within the rods. Optimal frequencies can be determined experimentally.

Best results are achieved when the frequency or current amplitude of the high frequency current provided by the high frequency power supply 21 is regulated such that the temperature of the entire volume of the silicon body is maintained within a 50° C. temperature range during at least a majority of the period of time when silicon is being deposited. Ideally, the temperature will be maintained within the 50° C. temperature range during the entire silicon deposition process, but in commercial operation, it may not be practical to maintain the entire volume of a rod within a 50° C. temperature range during the entire silicon deposition process, such as during the early stages of silicon deposition after preheating. Uniform temperature operation should be established as soon as practical and thereafter maintained during the remainder of the growth process until rods of a desired diameter for produced. At that point, the power supply 21 is de-energized and the rods allowed to cool. It is believed that polysilicon rods of up to 300 mm or more in diameter can be produced in this manner. Such rods should have a stress of no more that 11 MPa throughout their entire volumes.

The following calculations are the approximate depths of current flow from the outer surface of the rods 14 due to the skin effect with a power supply at frequencies of 60 Hz, 2 kHz, 20 kHz, 200 kHz, and 800 kHz. Note that these skin depths are independent of the effects discussed above. The formula to determine skin depth is ${\delta = \frac{1}{2_{\sqrt{\pi \quad f\quad {\mu\sigma}}}}},$

in which δ is the skin depth in meters, ƒ is the frequency in hertz, μ is the magnetic permeability, and σ is the conductivity. The term μ is μ=μ_(o)*μ_(r), where μ_(o) is the permeability of free space (4π*10⁻⁷ H/m), and μ_(r) is a scaling term for the conductor. For silicon, μ_(r) (relative permeability) is very nearly 1. The resistivity ρ. of silicon at 815° C. was found to be 0.03 Ω*cm. Since conductivity σ=1/ρ, a value of 3333 siemens/meter was used for conductivity. ${\delta \left( {f = 60} \right)} = {{\frac{1}{2_{\sqrt{60*\pi*\mu*3333}}}1125\quad {mm}} = {44.29\quad {inches}}}$ ${\delta \left( {f = {2*10^{3}}} \right)} = {\frac{1}{2_{\sqrt{2*10^{3}*\pi*\mu*3333}}} = {{195\quad {mm}} = {7.68\quad {inches}}}}$ ${\delta \left( {f = {20*10^{3}}} \right)} = {\frac{1}{2_{\sqrt{20*10^{3}*\pi*\mu*3333}}} = {{61.64\quad {mm}} = {2.427\quad {inches}}}}$ ${\delta \left( {f = {200*10^{3}}} \right)} = {\frac{1}{2_{\sqrt{200*10^{3}*\pi*3333}}} = {{19.5\quad {mm}} = {0.768\quad {inches}}}}$ ${\delta \left( {f = {800*10^{3}}} \right)} = {\frac{1}{2_{\sqrt{800*10^{3}*\pi*\mu*3333}}} = {{9.75\quad {mm}} = {0.384\quad {inches}}}}$

The skin depth value δ is the depth from the surface of the rod of 67% of the current. The current falls off exponentially from the outer surface toward the center of the conductor. These calculations show that at a frequency of 60 Hz, the current will not be affected by the skin effect in 150 mm rods. At a frequency of 200 kHz, 67% of the current will run in the outer 19.5 mm of the radius and at a frequency of 800 kHz, 67% of the current will flow in the outer 9.75 mm of radius. It should be noted that the temperature of the rods can be adjusted by varying the current amplitude or the frequency of the power supply.

As an example, silicon rods 150 mm in diameter can be grown in a reactor of the type shown in FIG. 1. Silicon starter filaments 17 will be preheated by initially supplying a low frequency current at a voltage of 26,000 volts and a frequency of 60 Hz to the filaments. After the silicon heats up beyond a temperature of 200° C., the voltage is decreased to about 1,700 volts and the low frequency current is adjusted, as needed, to provide a desired silicon deposition surface temperature of about 825° C. Monosilane gas, is fed into the reactor through the gas nozzles 13 and the gas reacts to deposit polycrystalline silicon 19 on the surfaces of the silicon starter filaments 17. The deposited silicon builds up to form polycrystalline silicon rods 14. Initially the current is 25 amps. As the rods increase in diameter, the current is steadily increased and the voltage is decreased to keep the silicon deposition surface at a constant temperature of about 825° C. At a rod diameter of about 50 mm, at which point the current is about 300 amps at a voltage of about 800 volts, a sensor 23 signals the computer control system 24 to operate the switch 22. The switch turns off the low frequency power supply 20 and connects the high frequency power supply 21, which provides high frequency current, at about 200 kilohertz, sufficient to maintain the surfaces of the rods at about 825° C. When operating at this high frequency, heating current migrates to the surface of a rod because of the “skin effect.” The high frequency power supply delivers current at a frequency such that at least about 70% of the current is concentrated in the outer 15% of the rods. As silicon continues to deposit on the deposition surfaces of the growing rods, the electrical current and voltage are adjusted, as needed, such that the temperature of the entire volume of the silicon body is maintained within a 50° C. temperature range during substantially the entire period of growth of the rod beyond 50 mm. The amperage and voltage are varied, as the diameters of the rods increase to 150 mm, to an ending current of about 1500 amps at a voltage of 400 volts. When the rods reach a size of 150 mm in diameter, the power supply 21 is de-energized and the rods allowed to cool. FIG. 4 illustrates the narrow temperature range possible for a 150 mm rod when current is applied at 200 kHz. It is calculated that the such rods will have a stress that is not greater than 6 MPa throughout the entire volume of the rods, as shown in FIG. 5.

Such uses of a high frequency power supply in the range of 2 kHz to 800 kHz result in great improvements in rods produced by CVD. It is expected that the rods, up to 300 mm in diameter, made using high frequency heating according the present invention will have a stress of no more than 11 MPa throughout their entire volume. Such rods will be sufficiently tough that failure due to the stress produced by external heating will be reduced and likely eliminated altogether. It should be possible to grow rods having a diameter of 300 mm or more. The rod diameter limit will not be based on brittleness, but instead on such things as maximum current available, reactor geometry, electrode load and current capability, reactor cooling, and the like.

It will be apparent to those having ordinary skill in the art that many changes may be made in the above-described embodiments of the invention. For example, other heat sources could be used with the reactor, particularly for the purpose of preheating filaments. Resistance heating is possible, and heat could be supplied by operation of a microwave or infrared heat source (not shown). Multiple heat sources can be operated, either sequentially or simultaneously, to maintain the desired temperature pattern within growing rods. Also, a high frequency power supply could be used advantageously for reactors where the precursor gas is a silicon-bearing gas other than monosilane. Such a power supply could be used with a trichlorosilane reactor of the type described in U.S. Pat. No. 4,724,160 of Arvidson et al. Accordingly, for the purpose of this disclosure, the term “silicon-bearing gas” is intended to mean any gas of the group consisting of silane (SiH₄), disilane (Si₂H₆), dichlorosilane (SiH₂Cl₂), trichlorosilane (SiHCl₃), silicon tetrachloride (SiCl₄), dibromosilane (SiH₂Br₂), tribromosilane (SiHBr₃), silicon tetrabromide (SiBr₄), diiodosilane (SiH₂I₂), triiodosilane (SiHI₃), silicon tetraiodide (SiI₄), and mixtures thereof. Therefore, the scope of the invention should be determined by the following claims. 

We claim:
 1. A silicon rod production apparatus, comprising: a reactor vessel containing at least one reaction chamber; a pair of electrodes extending into the reaction chamber; at least one silicon filament provided within the reaction chamber with the opposite ends of the filament connected to two different ones of the electrodes to heat the filament by electrical current flowing between the two electrodes; a source of a silicon-bearing gas connected to the interior of the vessel for supplying the gas into the reaction chamber to produce a reaction and to deposit polycrystalline silicon on the heated filament by chemical vapor deposition thereby producing a rod of polycrystalline silicon; and an electrical power supply that is connected to the electrodes and that supplies high frequency A.C. current having a frequency sufficiently high to produce a skin effect that causes a majority of the current to flow through an outer region of the silicon rod adjacent its outer surface in order to provide more heat at the outer region than at inner portions of the rod.
 2. An apparatus in accordance with claim 1 in which the current has a high frequency of at least 2 kilohertz.
 3. An apparatus in accordance with claim 2 in which the current frequency is in the range of 2 kilohertz to 800 kilohertz.
 4. An apparatus in accordance with claim 1 in which the power supply is a variable frequency power supply.
 5. An apparatus in accordance with claim 1 in which the silicon filament is u-shaped with two filament portions joined together at one end of each filament portion and connected at the other end of the filament portion to different ones of the electrodes.
 6. An apparatus in accordance with claim 1 in which the gas source is a source of a silane gas selected from the group consisting of monosilane, disilane, and mixtures thereof.
 7. An apparatus in accordance with claim 1 in which the gas source is a source of a halosilane gas. 